项目 |
技术指标 |
测试方法 |
||
|
H100A15 |
H150A15 |
H200A15 |
||
|
颜色 |
深灰色 |
深灰色 |
深灰色 |
-- |
|
厚度 |
0.5~3.0 |
0.5~3.0 |
0.5~3.0 |
ASTM D 374 |
|
密度(g/cc) |
2.5±0.2 |
3.2±0.2 |
3.4±0.2 |
ASTM D 792 |
|
硬度(Shore C) |
40~60(±5) |
40~60(±5) |
40~60(±5) |
ASTM D 2240 |
|
导热系数(W/m·K) |
1.0±0.2 |
1.5±0.2 |
2.0±0.2 |
ASTM D 5470 |
|
热阻(℃in2/W)(@20psi&1mm) |
≤2.0 |
≤1.5 |
≤1.0 |
ASTM D 5470 |
|
击穿电压(kV)(@1mm) |
＜0.1 |
＜0.1 |
＜0.1 |
ASTM D 149 |
|
体积电阻率(Ω.cm) |
≥1010 |
≥1010 |
≥1010 |
ASTM D 257 |
|
压缩比(%)(@50psi) |
≥15 |
≥15 |
≥15 |
ASTM D 575 |
|
拉伸强度 (MPa) |
≥0.5 |
≥0.5 |
≥0.3 |
ASTM D 412 |
|
延伸率(%) |
≥100 |
≥100 |
≥100 |
ASTM D 412 |
|
撕裂强度(N/mm) |
≥1.5 |
≥1.0 |
≥0.6 |
ASTM D 624 |
|
磁导率(@1MHz) |
15±5 |
15±5 |
15±5 |
SJ 20512 |
| 吸收频段（GHz) | 10-15 | 10-15 | 10-15 | GJB 2038A-2011 |
|
反射损耗dB/cm （@15GHz) |
94.88 | 69 | 51.8 | -- |
|
介电常数(@1MHz) |
≥2 |
≥2 |
≥2 |
ASTM D 150 |
|
介质损耗(@1MHz) |
≤0.1 |
≤0.1 |
≤0.1 |
|
|
使用温度 (℃) |
-40~160 |
-40~160 |
-40~160 |
IEC 60068-2-14 |
|
1.个人电脑和外围设备2.手机 3.数码相机4.CD-R/W、DVD 5.直流－直流转换器外围设备 6.DVD,蓝光光盘,录放机 7.车载电子设备(导航仪,音响设备) 8.非接触IC读卡器 9.芯片模块封装
|
|
5.实物图拍摄 莱尔德BSR-1/SS6M 吸波材料
吸波材料加工吸波材料加工无间距加工吸波材料(极大节省材料成本)MBSR-1/SS6M 0.25*305*305 MM吸波材料片材吸波材的应用
|
先进院(深圳)科技有限公司， © 2021 www.leird.cn. All rights reserved 粤ICP备2021051947号-1 © 2021 www.xianjinyuan.cn. All rights reserved 粤ICP备2021051947号-2